Hytrel® 5553FG NC010
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6s1qST_Hytrel-5553FG-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 55 Shore D High Performance Polyester Elastomer Developed for Food Contact Applications |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/2.16 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.4 | % | |
| Flow | 1.4 | % | |
| Water Absorption | |||
| 24 hr | 0.60 | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 56 | ||
| Shore D, 15 sec | 51 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 167 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 14.0 | MPa | |
| Break | 40.0 | MPa | |
| 5.0% Strain | 6.60 | MPa | |
| 10% Strain | 10.2 | MPa | |
| 100% Strain | 15.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 40 | % | |
| Break | > 300 | % | |
| Nominal Tensile Strain at Break | 600 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C, Partial Break | 150 | kJ/m² | |
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 70.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | -20.0 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 180 | °C | ISO 306/A50 |
| -- | 75.0 | °C | ISO 306/B50 |
| Melting Temperature 2 | 201 | °C | ISO 11357-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 4.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 19 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.80 | ||
| 1 MHz | 4.40 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 9.0E-3 | ||
| 1 MHz | 0.038 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Melt Density | 1.03 | g/cm³ |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPRENE® 5890F | SK Global Chemical | EPDM | SUPRENE® |
| Fainplast PVC GS 7802 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Flexus 7200 | Braskem | LLDPE | Flexus |
| Elastollan® S 65 A | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |
| Leostomer® SR2264 | Riken Technos Corp. | SBC | Leostomer® |