LNP™ THERMOCOMP™ PF008QS compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6rgFa0_LNP-THERMOCOMP-PF008QS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* PF008QS is a compound based on Nylon 6 resin containing 40% Glass Fiber. Added features of this material include: Heat Stabilized, Reduced Moisture. Also known as: LNP* THERMOCOMP* Compound PF-1008 HS RM Product reorder name: PF008QS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955, ISO 294-4 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.31 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.50 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12200 | MPa | ASTM D638 |
| -- | 11600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 152 | MPa | ASTM D638 |
| Break | 165 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 3.0 | % | ASTM D638 |
| Break | 3.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9580 | MPa | ASTM D790 |
| -- | 12000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 245 | MPa | ASTM D790 |
| -- | 263 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 2 | 18 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1100 | J/m | ASTM D4812 |
| 23°C 3 | 72 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 12.6 | J | ASTM D3763 |
| -- | 4.26 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 218 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 199 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 201 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.6E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 249 to 260 | °C | |
| Middle Temperature | 254 to 266 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 254 to 277 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan XCW-8980 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| DENKA EVA TEX NA610 | Denka Company Limited | EVA | DENKA EVA TEX |
| DuPure® R 50 | Ducor Petrochemicals BV | PP Homopolymer | DuPure® |
| Hanwha Total PP TB92R | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| KRATON® G1652 H | Kraton Polymers LLC | SEBS | KRATON® |