ULTEM™ 4000 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6qyGTk_ULTEM4000resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.67 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 3.1 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 - 0.30 | % | Internal method |
| Water Absorption (24 hr) | 0.11 | % | ASTM D570 |
| K (wear) Factor | Internal method | ||
| -- 1 | 62.0 | Internal method | |
| -- 2 | 1900 | Internal method | |
| PV Limit 3 | 2.1 | MPa·m/s | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 4(Break) | 82.7 | MPa | ASTM D638 |
| Tensile Elongation 5(Break) | 1.2 | % | ASTM D638 |
| Flexural Modulus 6(100 mm Span) | 8830 | MPa | ASTM D790 |
| Flexural Strength 7 | ASTM D790 | ||
| Yield, 100mm span | 114 | MPa | ASTM D790 |
| Fracture, 100mm span | 138 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| With steel-dynamic | 0.24 | ASTM D1894 | |
| With steel-static | 0.25 | ASTM D1894 | |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 33.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 64 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 160 | J/m | ASTM D4812 |
| Reverse Notch Izod Impact (3.20 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 212 | °C | ASTM D648 |
| Vicat Softening Temperature | 234 | °C | ASTM D1525 8 |
| CLTE - Flow | ASTM E831 | ||
| -40 to 40°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| -20 to 150°C | 1.6E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 105 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.838 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 10 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 338 - 360 | °C | |
| Middle Temperature | 343 - 366 | °C | |
| Front Temperature | 349 - 371 | °C | |
| Nozzle Temperature | 349 - 371 | °C | |
| Processing (Melt) Temp | 349 - 371 | °C | |
| Mold Temperature | 135 - 163 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | xE-10, PV=2000 psi-fpm vs Steel |
| 2 . | xE-10, PV=2000 psi-fpm vs Self |
| 3 . | 0.51 m/s |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 2.6 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC1-6009 | Spartech Polycom | ABS | Spartech |
| SynPlast™ NOTM-E | PolyOne Corporation | Tri (n-octyl) Trimellitate | SynPlast™ |
| BIOPLAST® GS 2189 | BIOTEC GmbH & Co. KG | TP, Unspecified | BIOPLAST® |
| HANWHA LLDPE 3325W | Hanwha Chemical | LLDPE | HANWHA LLDPE |
| Sylvin 9915-90 Blue 8364 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |