LNP™ LUBRILOY™ U2000A compound
| Category: | PPA , Polyphthalamide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6qrFSt_LNPLUBRILOYU2000Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY U2000A is a compound based on Polyphthalamide resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRILOY* Compound U Product reorder name: U2000A |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 1.6 - 1.8 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.6 - 1.8 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.7 | % | ISO 294-4 |
| Flow direction : 24 hours | 1.7 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3450 | MPa | ASTM D638 |
| -- | 3530 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 81.4 | MPa | ASTM D638 |
| Yield | 78.0 | MPa | ISO 527-2 |
| Fracture | 81.4 | MPa | ASTM D638 |
| Fracture | 78.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 3.6 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2 |
| Fracture | 3.6 | % | ASTM D638 |
| Fracture | 3.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2760 | MPa | ASTM D790 |
| -- | 2900 | MPa | ISO 178 |
| Flexural Stress | 109 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.23 | ASTM D3702 Modified | |
| With Self-Static | 0.23 | ASTM D3702 Modified | |
| Wear Factor - Washer | 20.5 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 2 | 5.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact (23°C) | 1300 | J/m | ASTM D4812 |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.80 | J | ASTM D3763 |
| -- | 16.3 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 164 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 3 | 183 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 106 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 103 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 7.1E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 304 - 316 | °C | |
| Middle Temperature | 304 - 316 | °C | |
| Front Temperature | 304 - 316 | °C | |
| Processing (Melt) Temp | 310 - 316 | °C | |
| Mold Temperature | 121 - 149 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 mm |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex WR-9120 J | SAMSUNG SDI CO., LTD. | ASA | Starex |
| Ultramid® B33 L 01 | BASF Corporation | Nylon 6 | Ultramid® |
| Geon™ Vinyl Flexible FC800 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Plaslube® TPX-PA6/6-95001 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |
| SHINSTRA WG65BS TKB | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |