4PROP® 2C11110
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4PROP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6qgVCa_4PROP-2C11110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PROP 2C11110 is a Recycled MFI 10 to 15 10% Talc Filled Copolymer Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1800 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 27.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 10 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Melting Temperature 1 | 165 | °C | ISO 11357 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 20 - 60 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIMONA® PVDF-SK | SIMONA AMERICA, Inc. | PVDF | SIMONA® |
| SOLPLAST TC 1000C | UTEKSOL d.o.o. | SBS | SOLPLAST TC |
| STABAMID® 26 FE 5 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| Next Nylon 66 Prime Series PG50-01NC | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Daelim Po1y® PH-630 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |