4PET® 9L22130 HHR
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | 4Plas |
| Trademark: | 4PET® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6pRFYE_4PET-9L22130-HHR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PET 9L22130 HHR is a Standard Flow 30% Glass Fibre Reinforced High Heat Resistant PET |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.59 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Vertical flow direction | 0.90 | % | |
| Flow direction | 0.20 | % | |
| Water Absorption 1(Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 800 | ppm | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | MPa | ISO 527-2/5 |
| Tensile Stress (Break, 23°C) | 135 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | ISO 180/1A |
| 23°C | 8.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 245 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 220 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 215 | °C | ISO 306/B |
| Melting Temperature 2 | 255 | °C | ISO 11357 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 140 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 90.0 - 140 | °C | |
| Injection Rate | Fast | ||
| Holding Pressure | 60.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 50 - 70 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 24 Hrs |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONYL 4006G25 | POLYROCKS CHEMICAL CO., LTD | Nylon 6 | PONYL |
| VINIKA® CD50EA | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| ASI POLYPROPYLENE 1259 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Enviramid® N1315STHL BK | Ravago Manufacturing Americas, LLC | Nylon 66 | Enviramid® |
| LG ABS XR404T | LG Chem Ltd. | ABS | LG ABS |