Orgalloy® LE 60LM
| Category: | Nylon 6 Alloy , Polyamide 6 Alloy |
| Manufacturer: | Arkema |
| Trademark: | Orgalloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6pEUii_Orgalloy-LE-60LM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Orgalloy® LE 60LM is a Polyamide 6 Alloy (Nylon 6 Alloy) product. It can be processed by blow molding, calendering, extrusion, film extrusion, injection molding, profile extrusion, resin transfer molding, sheet extrusion, or thermoforming and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1020 | 1020 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate (235°C/2.16 kg) | 1.50 | -- | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | |||
| Saturation | 6.4 | -- | % | |
| Equilibrium | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | -- | 700 | MPa | ISO 527-2 4 |
| Tensile Stress (Yield) | -- | 32.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Yield) | -- | 6.0 | % | ISO 527-2 6 |
| Nominal strain at break | -- | > 50 | % | ISO 527-2 7 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 9 |
| Electrical | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Comparative tracking index | -- | 600 | IEC 60112 10 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | -- | ISO 1210 11 | |
| Burning Behav. at thickness h (3.20 mm) | HB | -- | ISO 1210 12 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | 10 °C/min |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PC GP5001B | Sincerity Australia Pty Ltd. | PC | Sindustris PC |
| TAIRILAC AF3500 | Formosa Plastics Corporation | ABS | TAIRILAC |
| Chemiton CSF0NA 90 | Franplast S.r.l. | SEBS | Chemiton |
| Karina GRAY PVC COMPOUND -E 807-18/ 91-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 900 00 HB | LOXIM Industries Private Limited | ABS+Nylon | LOXIM |