Edgetek™ X TR2-20TA/000 NATURAL
| Category: | Copolyester , Copolyester |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6pBrUQ_Edgetek-X-TR2-20TA-000-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Edgetek™ engineering thermoplastics compounds made with Eastman Tritan™ copolyester offer a wide range of performance and properties with the addition of reinforcing additives. By utilizing Eastman Tritan™ copolyester these compounds provide chemical resistance, clarity, heat resistance and BPA-free solutions. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 to 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3380 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 2 | 51.7 | MPa | |
| Break 3 | 40.7 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield 4 | 5.0 | % | |
| Break 5 | 30 | % | |
| Flexural Modulus 6 | 3030 | MPa | ASTM D790 |
| Flexural Strength 7 | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Injection Molded) | 75 | J/m | ASTM D256A |
| Unnotched Izod Impact 8(23°C, 3.18 mm, Injection Molded) | 2100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 112 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 103 | °C | |
| CLTE | ASTM E831 | ||
| Flow : -30 to 30°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.4E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 266 to 282 | °C | |
| Mold Temperature | 60.0 to 65.6 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | 5.1 mm/min |
| 3 . | Type I, 5.1 mm/min |
| 4 . | 5.1 mm/min |
| 5 . | Type I, 5.1 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | Partial Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VINIKA® CC70DN | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Flexible | VINIKA® |
| Elastocon® 2825 | Elastocon TPE Technologies | TPE | Elastocon® |
| Hanwha Total PP GH23 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| PEARLSTICK® 45-60/18 | Lubrizol Advanced Materials, Inc. | TPU-Capro | PEARLSTICK® |
| 3M™ Dyneon™ Perfluoroelastomer PFE 7403WZ | 3M Advanced Materials Division | Perfluoroelastomer | 3M™ Dyneon™ Perfluoroelastomer |