LNP™ STAT-LOY™ PF303 compound
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-LOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6oZhyv_LNPSTATLOYPF303compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON PF303 is a compound based on Nylon 6 resin containing Glass Fiber. Added features of this material include: Antistat. Also known as: LNP* STAT-LOY* Compound PF-15 Product reorder name: PF303 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 5050 | MPa | ASTM D638 |
| Tensile Strength (Break) | 82.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 4090 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 96 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 650 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 183 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+9 - 1.0E+11 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 216 - 227 | °C | |
| Middle Temperature | 221 - 232 | °C | |
| Front Temperature | 227 - 238 | °C | |
| Processing (Melt) Temp | 232 | °C | |
| Mold Temperature | 82.2 - 93.3 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4590U | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Wellamid® GF30-60 XE-WBK | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| ICORENE® N1014 | ICO Polymers EMEA, A Division of A. Schulman | EVA | ICORENE® |
| LNP™ LUBRICOMP™ OCL36A compound | SABIC Innovative Plastics | PPS, Branched | LNP™ LUBRICOMP™ |
| PELPRENE™ S1002 | TOYOBO America, Inc. | TPEE | PELPRENE™ |