SCHULAMID® 6 GF 50 TSU
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6oMZVA_SCHULAMID-6-GF-50-TSU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% glass fiber reinforced, surface improved Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.62 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 23.5 | -- | cm³/10min | ISO 1133 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 18000 | 10000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 170 | 95.0 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.4 | 3.2 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 14800 | -- | MPa | ISO 178 |
| Flexural Stress | 235 | -- | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 1.9 | -- | % | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.2 | -- | kJ/m² | |
| 23°C | 6.0 | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 35 | -- | kJ/m² | |
| 23°C | 40 | 48 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 217 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 202 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 202 | -- | °C | ISO 306/A50 |
| -- | 207 | -- | °C | ISO 306/B50 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 275 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 31 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 725 | -- | °C | |
| 3.00 mm | 725 | -- | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 750 | -- | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 8008N-PE | TSRC Corporation | TPE | T-Blend® |
| Velocity® LGF60-PA66 | PlastiComp, Inc. | Nylon 66 | Velocity® |
| Zythane® 4065A | Alliance Polymers & Services | TPU-Polyester | Zythane® |
| Comai 101-1 BL | Comai Ltda | PP Copolymer | Comai |
| Honeywell PCTFE P4000TR | Honeywell | PCTFE | Honeywell PCTFE |