Infino HA-1011
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6nNi0b_Infino-HA-1011.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino HA-1011 is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 49 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 110 | ASTM D785 | |
| R-Scale | 104 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1800 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 46.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Break 3 | 59.0 | MPa | ASTM D638 |
| Break | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 120 | % | ASTM D638 |
| Break | 130 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 1900 | MPa | ASTM D790 |
| -- 6 | 2000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 69.0 | MPa | ASTM D790 |
| -- 8 | 73.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 45 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 710 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 390 | J/m | ASTM D256 |
| 23°C 10 | 54 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 127 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 120 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 106 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 98.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 117 | °C | ISO 306/B50 |
| -- | 118 | °C | ISO 306/B120 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 to 100 | °C | |
| Desiccant Dryer | 80.0 to 100 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 88.3 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 100 SI 2 HI HF | RTP Company | PP Copolymer | RTP |
| Zytel® 70G35HSRX BK099 | DuPont Performance Polymers | Nylon 66 | Zytel® |
| Valtec HP618 | INDELPRO, S.A. de C.V. | PP Homopolymer | Valtec |
| Dorlyl PVC GFA 61E | DORLYL S.N.C. | PVC, Unspecified | Dorlyl PVC |
| LNP™ THERMOCOMP™ Noryl_FM4025 compound | SABIC Innovative Plastics Europe | PPE+PS | LNP™ THERMOCOMP™ |