Petrotene® PP A3 T40 PRTA011 PH359
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Petrotene® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6mhrhU_Petrotene-PP-A3-T40-PRTA011-PH359.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polypropylene homopolymer with 40% mineral reinforced. Resistant to oil, grease and many solvents, good set of mechanical properties and excellent dimensional stability. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 5.0 to 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 0.050 | % | ASTM D570 |
| Ash Content | 37 to 43 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 31.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 12 | % | ASTM D638 |
| Flexural Modulus | 2500 | MPa | ASTM D790 |
| Flexural Strength | 49.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 25 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 3 | ASTM D648 | ||
| 0.45 MPa, Unannealed | 138 | °C | |
| 1.8 MPa, Unannealed | 80.0 | °C | |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ASTM D1525 4 |
| -- | 143 | °C | ASTM D1525 5 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 40 | kV/mm | ASTM D149 |
| Dissipation Factor (1 kHz) | 5.0E-3 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 230 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2°C/min |
| 4 . | Rate A (50°C/h), Loading 2 (50 N) |
| 5 . | Rate B (120°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4090 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Moplen HP2409 | LyondellBasell Industries | PP Homopolymer | Moplen |
| CALP 3400GE | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| HIDEN® M690 | YUHWA Korea Petrochemical Ind. Co., Ltd. | HDPE | HIDEN® |
| POLYFLAM® RPP 2000 | A. Schulman Europe | PP Homopolymer | POLYFLAM® |