Zytel® 158L NC010
| Category: | Nylon 612 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6lABWA_Zytel-158L-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Unreinforced Polyamide 612 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ||||
| Flow : 3.20 mm | 1.1 | -- | % | Internal Method |
| Across Flow | 1.4 | -- | % | ISO 294-4 |
| Flow | 1.3 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 3.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.3 | -- | % | |
| Viscosity Number | 120 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1500 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 62.0 | 52.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.5 | 19 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 35 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2050 | 1450 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 4.0 | kJ/m² | |
| 23°C | 4.0 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 5.0 | 4.0 | kJ/m² | |
| 23°C | 4.0 | 6.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 135 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 62.0 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 60.0 | -- | °C | ISO 11357-2 |
| Melting Temperature 2 | 218 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.2E-4 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 9.0E-5 | -- | cm/cm/°C | |
| Flow : 55 to 160°C | 1.7E-4 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 9.0E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 1.8E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 36 | 36 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.60 | -- | ||
| 1 MHz | 3.20 | -- | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.014 | -- | ||
| 1 MHz | 0.016 | -- |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.860 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 25 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | |
|---|---|---|---|---|
| Melt Density | 0.900 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2800 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.19 | -- | W/m/K |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ WCA901 resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |
| Generic PVC, Rigid - Glass Fiber | Generic | PVC, Rigid | Generic |
| EnDura® V91J | Precision Polymer Engineering Ltd. | Fluorelastomer | EnDura® |
| HiFill® PC / PET 2230 | Techmer Engineered Solutions | PC+PBT | HiFill® |
| Pier One POM AH900-NAT | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | Pier One POM |