Pebax® 7233 SA 01
| Category: | PEBA-Ether , Polyether Block Amide |
| Manufacturer: | Arkema |
| Trademark: | Pebax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6l3NXX_Pebax-7233-SA-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyether block amide Pebax® 7233 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. This SA grade is suitable for food contact applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | Internal Method | ||
| Across Flow : 24 hr, 4.00 mm | 1.5 | % | |
| Flow : 24 hr, 4.00 mm | 1.2 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.90 | % | |
| Equilibrium, 23°C, 50% RH | 0.70 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 69 | ||
| Shore D, 15 sec | 61 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 56.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Flexural Modulus | 510 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C, Complete Break | 10 | kJ/m² | |
| 23°C, Complete Break | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 164 | °C | ISO 306 |
| Melting Temperature | 174 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Processing (Melt) Temp | 230 to 290 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 5.0 to 7.0 | hr | |
| Melt Temperature | 220 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | Mold at 40°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FERREX® GPP20CC61HB RED | Ferro Corporation | PP Homopolymer | FERREX® |
| Generic Polyester, TP | Generic | Polyester, TP | Generic |
| Karina BLACK PVC COMPOUND -E 60820-48/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina RED PVC COMPOUND -E711D42/158-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LOXIM 340 01 HB | LOXIM Industries Private Limited | Nylon 6 | LOXIM |