UBE NYLON 5034 FDX17 is a high viscosity Polyamide 6/6.6 copolymer containing an anti block agent. The material is especially suitable as outer layer for air-cooled blown film (asymmetric layer structure). Typical applications are for pouches and thermoformed products.

General Information
Additive	Anti-caking agent
Features	Anti-caking property Workability, good Definition, high Compliance of Food Exposure High shrinkage Viscosity, High
Uses	Films
Agency Ratings	European food contact, not rated
Forms	Particle
Processing Method	Blow film Thermoforming

Physical	Nominal Value	Unit	Test Method
Density	1.14	g/cm³	ISO 1183

Mechanical	Nominal Value	Test Method
Coefficient of Friction		ASTM D1894
With self-dynamics	0.30	ASTM D1894
With Self-Static	0.30	ASTM D1894

Films	Nominal Value	Unit	Test Method
Secant Modulus - MD (Cast Film)	550	MPa	ASTM D882
Tensile Strength - MD			ASTM D882
Yield, extruded film	27.0	MPa	ASTM D882
Fracture, extruded film	115	MPa	ASTM D882
Tensile Elongation - MD (Fracture, Extruded Film)	650	%	ASTM D882

Thermal	Nominal Value	Unit	Test Method
Melting Temperature (DSC)	197	°C	ISO 3146

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	ASTM D257

Optical	Nominal Value	Unit	Test Method
Gardner Gloss	140		ASTM D523
Haze	3.5	%	ASTM D1003

Additional Information
The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Oxygen Permeability, ASTM D3985: 37 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 4.09Extractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 80/20Water Vapor Permeability, JIS Z0208: 90 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 15 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <10 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <10 hole/0.04 m²

Additional Information

The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357.The value listed as Surface Resistivity, ASTM D257, was tested in accordance with UBE test methods.Oxygen Permeability, ASTM D3985: 37 ml/m²/dayRelative Viscosity, JIS K6810, 96% H2SO4, conc. 1.0 g/100 ml: 4.09Extractable Content, JIS K6810: <1.0 wt%Molecular Ratio, PA6/PA6.6: 80/20Water Vapor Permeability, JIS Z0208: 90 g/m²/dayPiercing Strength, JAS P1019, Cast Film: 9.5 NPiercing Elongation, JAS P1019, Cast Film: 15 mmFlex Crack Resistance, MIL B131B, 23°C, 1000 cycle, Cast Film: <10 hole/0.04 m²Gelbo Test, MIL B131B, 5°C, 100 cycle, Cast Film: <10 hole/0.04 m²

Category:	Nylon 66/6 , Polyamide 66/6 Copolymer
Manufacturer:	UBE Engineering Plastics, S.A.
Trademark:	UBE Nylon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6kq5eY_UBE-Nylon-5034-FDX17.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
MonoSol® M-9500	MonoSol, LLC	PVOH	MonoSol®
Ultradur® B 2550 FC	BASF Corporation	PBT	Ultradur®
LITEN LS 87	UNIPETROL RPA	PE Copolymer	LITEN
Mafill® CR C 4044	Ravago Group	PP Copolymer	Mafill®
POLYfill PPHC T8040	Polykemi AB	PP, Unspecified	POLYfill