LNP™ LUBRICOMP™ ECL36XXQ compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6idVK6_LNP-LUBRICOMP-ECL36XXQ-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* ECL36XXQ is a compound based on Polyetherimide containing 30% Carbon Fiber, 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound ECL36XXQ Product reorder name: ECL36XXQ |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.39 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.010 to 0.050 | % | |
| Across Flow : 24 hr | 0.10 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 32900 | MPa | ASTM D638 |
| -- | 30400 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 222 | MPa | ASTM D638 |
| Break | 226 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 0.90 | % | ASTM D638 |
| Break | 1.0 | % | ISO 527-2/5 |
| Flexural Modulus 4(50.0 mm Span) | 26300 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 324 | MPa | ASTM D790 |
| Poisson's Ratio | 0.43 | ASTM D638 | |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.39 | ||
| vs. Itself - Static | 0.42 | ||
| Wear Factor - Washer | 22.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 410 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 11.7 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 208 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+4 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 343 to 354 | °C | |
| Middle Temperature | 354 to 366 | °C | |
| Front Temperature | 366 to 377 | °C | |
| Processing (Melt) Temp | 360 to 366 | °C | |
| Mold Temperature | 121 to 149 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2563 FR | RTP Company | PC+ABS | RTP |
| Nanjing Hongrui PP P1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| NEOFLON™ M-400H | DAIKIN AMERICA, INC. | PCTFE | NEOFLON™ |
| ExxonMobil™ HDPE HMA 025 | ExxonMobil Chemical | HDPE, UHMW | ExxonMobil™ HDPE |
| LEXAN™ XLS1210 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |