LNP™ LUBRICOMP™ Lexan_WR2210 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6iSUeD_LNPLUBRICOMPLexanWR2210compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP LEXAN_WR2210 compound is based on an aternative polymeric wear technology and does not contain silicones. LEXAN WR2210 has superior processability (flow similar to LEXAN 121) and part appearance. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 103 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 2 | 2000 | MPa | ASTM D638 |
| Tensile Strength 3 | ASTM D638 | ||
| Yield | 55.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ASTM D638 |
| Tensile Elongation 4 | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 100 | % | ASTM D638 |
| Flexural Modulus | |||
| 100mm span 5 | 2200 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Strength 7(Yield, 100 mm Span) | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/2C |
| Notched Izod Impact | |||
| -20°C | 150 | J/m | ASTM D256 |
| 23°C | 600 | J/m | ASTM D256 |
| -30°C 8 | 20 | kJ/m² | ISO 180/1A |
| 23°C 9 | 45 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 150 | °C | ASTM D1525 10 |
| -- | 142 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (23 to 80°C) | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.20 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | HB | UL 94 | |
| Oxygen Index | 27 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 260 - 280 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESN Noir P40 TL01 | Arkema | Nylon 11 | Rilsan® |
| MAZMID 6.10 | Mazzaferro Indústria e Comércio de Polímeros e Fibras Ltda. | Nylon 610 | MAZMID |
| Desmopan® DP 3072D | Covestro - PUR | TPU-Polyester | Desmopan® |
| Indothene HD 45GP004 | Reliance Industries Limited | HDPE | Indothene HD |
| Infino AR-6508 | SAMSUNG SDI CO., LTD. | PBT+PET | Infino |