MAJORIS SG300 - 8229
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6iQIw0_MAJORIS-SG300---8229.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAJORIS SG300 - 8229 is a special 30 % long glass fibre reinforced polyamide 6 intended for Injection moulding. APPLICATIONS MAJORIS SG300 - 8229 has been developed especially for very demanding applications in automotive industry and electrical parts. Products requiring excellent combination between thermal and mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 to 0.80 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12900 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 220 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | % | ISO 527-2 |
| Flexural Modulus | 11000 | MPa | ISO 178 |
| Flexural Stress | 320 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 13 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 42 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | IEC 60695-2-12 |
| Oxygen Index | 23 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 255 to 275 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Nozzle Temperature | 265 to 275 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 95.0 to 120 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 60.0 to 80.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravamid® AMGF15/15 H BK | Ravago Group | Nylon 66 | Ravamid® |
| RapidVac™ VA-1710 | Innovative Polymers, Inc. | TSU | RapidVac™ |
| Melthene® -M M5002D | TOSOH Corporation | Polyolefin, Unspecified | Melthene® -M |
| ADDILENE PMD 50218 | ADDIPLAST | PP, Unspecified | ADDILENE |
| Karina IVORY PVC COMPOUND 757-35/ 1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |