LNP™ THERMOCOMP™ Lexan_LGK5030 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6hvcfa_LNP-THERMOCOMP-Lexan-LGK5030-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass reinforced. Flame retardant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.61 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.050 to 0.25 | % | |
| Across Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Water Absorption (24 hr) | 0.14 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 142 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 3(50.0 mm Span) | 10700 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 50.0 mm Span) | 187 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 144 | °C | ASTM D648 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 4.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 16 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-1 | ||
| 2.79 mm | V-0 | ||
| 3.61 mm | 5VA |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polyethylene Lumicene® M 2711 PCE | TOTAL Refining & Chemicals | LLDPE | TOTAL Polyethylene |
| Firestone CL200-001 | Firestone Textiles Company | Nylon 6 | Firestone |
| Hostaform® MT12U03 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| KOPLA PET KEG1020 | KOPLA Co., Ltd. | PET | KOPLA PET |
| INEOS PP 102-GF02 | INEOS Olefins & Polymers Europe | PP Homopolymer | INEOS PP |