LNP™ LUBRICOMP™ DFL329 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6hGMZQ_LNP-LUBRICOMP-DFL329-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DFL329 is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features of this material include: Flame Retardant, Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound DFL-4032 FR Product reorder name: DFL329 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.49 | % | ISO 294-4 |
| Flow : 24 hr | 0.33 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.13 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 4340 | MPa | ASTM D638 |
| -- | 4500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 75.6 | MPa | ASTM D638 |
| Break | 74.3 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | |||
| -- | 4270 | MPa | ASTM D790 |
| -- | 4600 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 129 | MPa | ASTM D790 |
| -- | 127 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 180 | J/m | ASTM D256 |
| 23°C 2 | 9.9 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 550 | J/m | ASTM D4812 |
| 23°C 3 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 18.4 | J | ASTM D3763 |
| -- | 3.88 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 142 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 141 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 5.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.70 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Durez® 25378 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Durez® |
| Kepamid® 1320GF | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| LUVOCOM® 1301-8331-2 | Lehmann & Voss & Co. | PPS | LUVOCOM® |
| Lushan PJ-1 | Guangzhou Lushan New Materials Co., Ltd | PP, Unspecified | Lushan |
| ULTEM™ ATX200R resin | SABIC Innovative Plastics | PEI+PCE | ULTEM™ |