EMERGE™ PC 8430-6
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6gxnny_EMERGE-PC-8430-6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8430-6 advanced resin is a transparent, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. The resin is designed to meet the German norm DIN VDE-0472/Part 815 on halogens. This resin combines good mechanical and high heat properties. EMERGE™ PC 8430-6 contains release agent and is UV-stabilized. EMERGE ™ PC 8430-6 has a UL 94 V-0 rating at 1.8 mm and a UL 94 V-2 rating at 0.75 mm. Applications
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/B |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 60.0 | MPa | |
| Break | 70.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 110 | % | |
| Flexural Modulus | 2350 | MPa | ISO 178 |
| Flexural Stress | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 80 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 145 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 126 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed | 142 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Ball Indentation Temperature | > 125 | °C | IEC 60335-1 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | 17 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 1 Hz | 2.70 | ||
| 50 Hz | 2.70 | ||
| Dissipation Factor | IEC 60250 | ||
| 1 Hz | 1.0E-3 | ||
| 50 Hz | 1.0E-3 | ||
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm 1 | V-2 | ||
| 1.50 mm 2 | V-2 | ||
| 1.80 mm | V-0 | ||
| 3.00 mm 3 | V-0 | ||
| Glow Wire Flammability Index 4 | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature 5 | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 800 | °C | |
| 3.00 mm | 800 | °C | |
| Oxygen Index 6 | 35 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 7 | 87.0 to 91.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 320 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 5 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 6 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 7 . | standard tints |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Chiao Fu PBT PBT819B30 NAT | Chiao Fu Enterprises Co., Ltd. | PBT | Chiao Fu PBT |
| Chemical Resources PP 400 | Chemical Resources, Inc. | PP Homopolymer | Chemical Resources |
| Ecomass® 1850ZN66T1 | Ecomass Technologies | Nylon 6 | Ecomass® |
| Generic PPA - Glass Fiber, Long | Generic | PPA | Generic |
| Kazan HDPE 293-5-7D1K | Kazanorgsintez Joint Stock Company | HDPE | Kazan HDPE |