Order Products : sales@su-jiao.com
LEXAN™ XHT3141 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6gnMlG_LEXANXHT3141resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XHT3141 is a high flow, high heat polycarbonate copolymer. It is available in a range of opaque and limited transparent colors. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 33 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.90 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2700 | MPa | ASTM D638 |
| -- | 2500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 70.0 | MPa | ASTM D638 |
| Yield | 70.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 55.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 70 | % | ASTM D638 |
| Fracture | 70 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2600 | MPa | ASTM D790 |
| -- 7 | 2500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 80.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C | 11 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 55 | J/m | ASTM D256 |
| 23°C | 97 | J/m | ASTM D256 |
| -30°C 11 | 9.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 68.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 166 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 14 | 164 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 156 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 15 | 152 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 170 | °C | ASTM D1525, ISO 306/B120 11 16 |
| -- | 168 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Thermal Conductivity (25°C) | 0.20 | W/m/K | ASTM C177 |
| RTI Elec | 150 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI | 150 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+17 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 23 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 100 Hz | 2.90 | ASTM D150 | |
| 1 MHz | 2.80 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 100 Hz | 0.031 | ASTM D150 | |
| 1 MHz | 0.011 | ASTM D150 | |
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 875 | °C | IEC 60695-2-13 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Metallized Haze Onset | 165 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 280 - 315 | °C | |
| Middle Temperature | 290 - 335 | °C | |
| Front Temperature | 300 - 345 | °C | |
| Nozzle Temperature | 285 - 325 | °C | |
| Processing (Melt) Temp | 300 - 345 | °C | |
| Mold Temperature | 95.0 - 130 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 90 | rpm | |
| Vent Depth | 0.025 - 0.080 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 mm |
| 15 . | 80*10*4 mm |
| 16 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC 8266 Natural | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Axiall PVC 7800 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Optema™ TC 114 Blown | ExxonMobil Chemical | EMA | Optema™ |
| Sylvin 8205-75UV Grey 9627 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9067-90 Grey 991 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |