SABIC® LDPE 2102X0
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6gfgiT_SABIC-LDPE-2102X0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2102X0 is a Low Density Polyethylene natural resin typically used for the production of Medium/High Voltage power cable insulation using the direct peroxide addition. SABIC® LDPE 2102X0 is a non-additivated and non-stabilized LDPE. It exhibits very high cleanliness and consistent purity. Sufficient antioxidant should be added to meet specific ageing requirements. Application Peroxide cross-linkable insulation for Medium/High Voltage power cable. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 45 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 175 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 9.00 | MPa | |
| Break | 13.0 | MPa | |
| Tensile Strain (Break) | 850 | % | ISO 527-2 |
| Modulus of Elasticity | 250 | MPa | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat of Fusion | 110 | J/g | DIN 53765 |
| Vicat Softening Temperature | 89.0 | °C | ISO 306/A |
| Melting Temperature (DSC) | 108 | °C | DIN 53765 |
| Peak Crystallization Temperature (DSC) | 97.0 | °C | Internal Method |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 8.5E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength 1 | > 30 | kV/mm | ASTM D149 |
| Dielectric Constant (60 Hz) | 2.20 | ASTM D150 | |
| Dissipation Factor (60 Hz) | 5.0E-4 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | 2000 V/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL EF-6155 UV | Teknor Apex Company | TPE | Telcar® |
| Unipren® Elastomers A3 PRTA010 55A UP305 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| Nypol® PA A3 G40 M3 NTLA014 NR448 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| apigo® D 40T | API SpA | TPO (POE) | apigo® |
| Cellophane™ 360MSB | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |