Akulon® Ultraflow K-FHGM35
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® Ultraflow |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6gTN7T_Akulon-Ultraflow-K-FHGM35.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Akulon® Ultraflow K-FHGM35 is a Polyamide 6 (Nylon 6) material filled with 15% glass fiber and 25% mineral. It is available in North America. Important attributes of Akulon® Ultraflow K-FHGM35 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.50 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.30 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 120 | 65.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.5 | 5.0 | % | ISO 527-2 |
| Flexural Modulus | 7700 | -- | MPa | ISO 178 |
| Flexural Stress | 165 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | 4.0 | kJ/m² | |
| 23°C | 5.0 | 6.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | 30 | kJ/m² | |
| 23°C | 35 | 45 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 3.5E-5 | -- | cm/cm/°C | |
| Transverse | 5.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength | 35 | 30 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | 3.50 | 14.0 | ||
| 1 MHz | 3.30 | 4.50 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 5.0E-3 | 0.32 | ||
| 1 MHz | 0.014 | 0.12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 250 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Nozzle Temperature | 250 to 280 | °C | |
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Texalan® 6 Series 690A | Austin Novel Materials Co. Ltd. | TPU-Ester/Ether | Texalan® 6 Series |
| 4MID® 9A23300 X | 4Plas | Nylon 66 | 4MID® |
| Chiao Fu PP PP212GM30 NAT | Chiao Fu Enterprises Co., Ltd. | PP, Unspecified | Chiao Fu PP |
| Cheng Yu 3200 | Cheng Yu Plastic Company Limited | TPE | Cheng Yu |
| Huaxia Shenzhou PVDF DS205 | Shandong Huaxia Shenzhou New Material Co., Ltd. | PVDF | Huaxia Shenzhou |