Huafon EP127
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Huafon Group Co., Ltd. |
| Trademark: | Huafon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6gQetg_Huafon-EP127.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EP127 is an injection molding Nylon 66 resin. This resin offers a well-balanced combination of engineering properties characterized by good toughness; high impact; good surface lubricity: abrasion resistance; self-extinguishment. Typical Applications As an injection molding resin, EP127 is suitable for the production of cable ties and other molding product. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 70 | g/10 min | ISO 1133 |
| Particle Size | 1.40 to 2.00 | g/100 pellets | Internal Method |
| Relative Viscosity | 2.62 to 2.72 | Internal Method | |
| Water Content | < 4000 | mg/kg | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | 74.6 | MPa | ISO 527-2 |
| Tensile Strain 2(Break) | 69 | % | ISO 527-2 |
| Flexural Modulus 3 | 2640 | MPa | ISO 178 |
| Flexural Stress 4 | 97.6 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 5(23°C) | 6.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Annealed | 184 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 66.1 | °C | ISO 75-2/A |
| Vicat Softening Temperature 7 | 239 | °C | ISO 306/B120 |
| Peak Melting Temperature 8 | 267 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating 9 | UL 94 | ||
| 1.00 mm | V-2 | ||
| 1.60 mm | V-2 | ||
| 3.00 mm | V-2 |
| Note Message | |
|---|---|
| 1 . | 48h/23°C/50%RH |
| 2 . | 48h/23°C/50%RH |
| 3 . | 48h/23°C/50%RH |
| 4 . | 48h/23°C/50%RH |
| 5 . | 48h/23°C/50%RH |
| 6 . | 48h/23°C/50%RH |
| 7 . | 48h/23°C/50%RH |
| 8 . | 10°C/min |
| 9 . | 48h/23°C/50%RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4004 | RTP Company | PPA | RTP |
| RheTech Polypropylene GC20P255-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| TEKNIFLEX® PGA 18200 | Tekni-Films, a div of Tekni-Plex | Film, PETG/PCTFE | TEKNIFLEX® |
| Stat-Rite® E1150 | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Stat-Rite® |
| Lupoy® 1302HP-10 | LG Chem Ltd. | PC | Lupoy® |