Petrothene® LT602901
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6gOqEB_Petrothene-LT602901.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Petrothene LT602901 is a high density polyethylene sheet extrusion grade with excellent extrusion characteristics and low warpage. The resulting sheet exhibits good stiffness and impact properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.960 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 30.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1400 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 1550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact | 53.9 | J/cm | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 75.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wondel® P PM6 | Nanjing Julong Engineering Plastics Co., LTD | PP, Unspecified | Wondel® P |
| Yuyao PP TL203 | Yuyao Tenglong Plastics Co., Ltd. | PP, Unspecified | Yuyao PP |
| Nanjing Hongrui PA6 B326 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 6 | Nanjing Hongrui PA6 |
| En Chuan 6012 | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| Infino ASF-9810FL | LOTTE ADVANCED MATERIALS CO., LTD. | PBT | Infino |