Braskem PE TN7006
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6fgDMc_Braskem-PE-TN7006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TN7006 is a low-density polyethylene (LDPE) specially developed for coextruded films and lamination. The resin presents a great combination among mechanical, optical and stiffness properties. Besides TN7006 has low gels content which ensure a production of excellent appearance films. This product is identified as PE 114 according to ASTM D-4976-04a standard specification. Additives: No additives Application: High clarity films for coextruded food packaging, such as: cheese, meat, sausages, sliced ham, etc. Cast films for table cloth, curtains and laminated tissues. Flexible bottles for solids, liquids or pasties products for hygiene and cleanness. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.924 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 140 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 170 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 25.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 350 | % | |
| TD : Break, 50 µm, Blown Film | 700 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 170 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, Blown Film | 310 | g | |
| TD : 50 µm, Blown Film | 250 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 50.0 µm, Blown Film | 60 | ||
| 60°, 50.0 µm, Blown Film | 86 | ||
| Haze (50.0 µm, Blown Film) | 8.5 | % | ASTM D1003 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Blow Molding Temperature 1 | |||
| Mass Temperature | 180 to 185 | °C | |
| Temperature Profile | 150 to 185 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0mm Die Gap, 2.0 to 3.0:1 Blow Up Ratio |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC P6185 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Thermoset Plastics 210 | Thermoset, Lord Chemical Products | Epoxy | Thermoset Plastics |
| Baydur® 645 (20 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Diamond ABS 7501 | Network Polymers, Inc. | ABS | Diamond ABS |
| EnviroNylon N6 | West Michigan Compounding | Nylon 6 | EnviroNylon |