4LAC® 10H10500
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | 4Plas |
| Trademark: | 4LAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6fbXE1_4LAC-10H10500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4LAC 10H10500 is a Low Flow Heat Stabilised ABS |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Across Flow | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2400 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 20 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -30°C | 8.0 | kJ/m² | ISO 180/1A |
| 23°C | 18 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 99.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 105 | °C | ISO 306/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 700 | °C | IEC 60695-2-12 |
| 2.00 mm | 700 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 50.0 - 60.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 50.0 - 100 | MPa | |
| Screw Speed | 200 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 30 - 50 °CBack Pressure: Low |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech H706 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 46 | Sup-tech |
| CompaMid® PA 6.6 HI | DimeLika Plast GmbH | Nylon 66 | CompaMid® |
| FHR Polypropylene P4G4K-205 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| Guang Sung PVC GPMA80T | Guang Sung Plastics (GSPL) | PVC, Unspecified | Guang Sung PVC |
| LNP™ FARADEX™ AS003 compound | SABIC Innovative Plastics | ABS | LNP™ FARADEX™ |