Sarlink® TPE OM-2145 BLACK 404
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6f2zQR_Sarlink-TPE-OM-2145-BLACK-404.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sarlink®TPE OM-2145 BLACK 404 is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Sarlink®The main characteristics of TPE OM-2145 BLACK 404 are: flame retardant/rated flame. Sarlink®The typical application field of TPE OM-2145 BLACK 404 is: automobile industry |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 2.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 50 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 7.58 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 600 | % | ASTM D412 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 138 - 160 | °C | |
| Middle Temperature | 182 - 199 | °C | |
| Front Temperature | 182 - 199 | °C | |
| Nozzle Temperature | 193 - 210 | °C | |
| Processing (Melt) Temp | 177 - 199 | °C | |
| Mold Temperature | 4.44 - 48.9 | °C | |
| Injection Pressure | 1.38 - 5.52 | MPa | |
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 100 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 潮湿会使材料降解。建议进行干燥处理。可以把材料放入除湿干燥机，在140°F的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 138 - 149 | °C | |
| Cylinder Zone 2 Temp. | 149 - 160 | °C | |
| Cylinder Zone 3 Temp. | 160 - 182 | °C | |
| Cylinder Zone 5 Temp. | 171 - 193 | °C | |
| Die Temperature | 182 - 204 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 280.8 | RTP Company | Nylon 66 | RTP |
| RTP 1000 GB 10 | RTP Company | PBT | RTP |
| ALAMID® 6.6 CF 40 SCHWARZ-9908 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| Bergamid™ A70 G25 BK062 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| LG PVC LS100S | LG Chem Ltd. | PVC, Unspecified | LG PVC |