Lastilac RT K/10
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Lastilac |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6f1nqq_Lastilac-RT-K-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Acrylonitrile-Butadiene-Styrene copolymer (ABS). Carbon fibre. High dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.80 | % | |
| Flow : 2.00 mm | 0.25 to 0.40 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 8300 | MPa | |
| 60°C | 7500 | MPa | |
| 90°C | 6000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 90°C | 30.0 | MPa | |
| Break, 23°C | 60.0 | MPa | |
| Break, 60°C | 45.0 | MPa | |
| Break, 90°C | 30.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 90°C | 0.60 | % | |
| Break, 23°C | 0.70 | % | |
| Break, 60°C | 0.70 | % | |
| Break, 90°C | 0.70 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 4.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 10 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 50 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 105 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 75.0 | °C | |
| Vicat Softening Temperature | 105 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 5.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+3 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Delta ABR-1G30/1 | Delta Polymers | ABS | Delta |
| Ferro PP TPP40AC73NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Globalene® 868H | Lee Chang Yung Chemical Industry Corp. | PP Random Copolymer | Globalene® |
| LUVOCOM® 1-8562 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| PIVINEL™ S-893-LF | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |