Viprene™ P65A-22U-NAT
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Alliance Polymers & Services |
| Trademark: | Viprene™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6eh51O_Viprene-P65A-22U-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Viprene™ P65A-22U-NAT is a UV and Heat Stabilized TPV (thermoplastic vulcanizate elastomer). This material can be easily procesed by extrusion or injection molding. It exhibits easy flowing characteristics. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.970 | g/cm³ | ISO 2781 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 65 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| 100% strain | 2.50 | MPa | ISO 37 |
| 300% strain | 3.80 | MPa | ISO 37 |
| Tensile Stress (Break) | 7.20 | MPa | ISO 37 |
| Tensile Elongation (Break) | 550 | % | ISO 37 |
| Tear Strength | 40 | kN/m | ISO 34-1 |
| Compression Set (70°C, 22 hr) | 22 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -60.0 | °C | ASTM D746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | HB | UL 94 | |
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 180 | °C | |
| Middle Temperature | 185 | °C | |
| Front Temperature | 185 | °C | |
| Nozzle Temperature | 185 - 220 | °C | |
| Processing (Melt) Temp | 190 - 230 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Back Pressure | 0.500 - 0.850 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Clamp Tonnage | 4.0 - 7.0 | kN/cm² |
| Injection instructions |
|---|
| Injection Speed: 50 mm/sec or more |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 185 | °C | |
| Cylinder Zone 3 Temp. | 185 | °C | |
| Die Temperature | 195 | °C |
| Extrusion instructions |
|---|
| Gate Temperature: 190°C (374°F)Die Pressure: 4.8 to 17 MPa (696 to 2465 psi) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoFlo 90A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| WPP PP PPHFGC-2 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| FERREX® GPP40CC90UL | Ferro Corporation | PP Homopolymer | FERREX® |
| Durethan® T 7141 00000 | LANXESS GmbH | PBT+PET | Durethan® |
| Sylvin 7868-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |