Infino WP-1089
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6c3aGH_Infino-WP-1089.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino WP-1089 is a Polycarbonate + ABS (PC+ABS) product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238, ISO 1133 | ||
| 250°C/10.0 kg | 47 | g/10 min | |
| 260°C/5.0 kg | 27 | g/10 min | |
| Molding Shrinkage | ASTM D955, ISO 2577 | ||
| Flow : 3.20 mm | 0.50 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.50 to 0.60 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| R-Scale | 108 | ASTM D785 | |
| R-Scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2100 | MPa | ASTM D638 |
| -- | 2100 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 53.0 | MPa | ASTM D638 |
| Yield | 52.0 | MPa | ISO 527-2/50 |
| Break 3 | 44.0 | MPa | ASTM D638 |
| Break | 45.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 4 | 80 | % | ASTM D638 |
| Break | 60 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 2200 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 76.0 | MPa | ASTM D790 |
| -- 8 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 51 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 390 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 200 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 590 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 420 | J/m | ASTM D256 |
| -30°C 10 | 32 | kJ/m² | ISO 180/1A |
| 23°C 11 | 46 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 6.40 mm | 130 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 4.00 mm | 123 | °C | ISO 75-2/B |
| 0.45 MPa, Annealed | 125 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 6.40 mm | 110 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 4.00 mm | 104 | °C | ISO 75-2/A |
| 1.8 MPa, Annealed, 4.00 mm | 105 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 126 | °C | ISO 306/B50 |
| CLTE | ASTM D696, ISO 11359-2 | ||
| Flow : 40 to 100°C | 8.1E-5 | cm/cm/°C | |
| Transverse : 40 to 100°C | 8.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 90.0 | °C | |
| Desiccant Dryer | 80.0 | °C | |
| Drying Time | |||
| -- | 4.0 | hr | |
| Desiccant Dryer | 4.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 260 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C | |
| Injection Pressure | 58.8 | MPa | |
| Back Pressure | 0.490 to 2.45 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4 mm |
| 10 . | Thickness 4 mm |
| 11 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sarlink® TPV 2440D | Teknor Apex Company | TPV | Sarlink® TPV |
| Vinylbond 95-950-80 | Colorite Polymers | PVC, Flexible | Vinylbond |
| KEBAFORM® C 2027 | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| MAJORIS FW350 | AD majoris | PP, Unspecified | MAJORIS |
| Polybutene-1 DP8911ME | LyondellBasell Industries | PB | Polybutene-1 |