Borealis PP VG621
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6byGxh_Borealis-PP-VG621.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VG621 is a 30% chemically coupled glass fibre reinforced polypropylene compound intended for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 86.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 6200 | MPa | ISO 178 |
| Flexural Stress | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 157 | °C | ISO 75-2/Be |
| 1.8 MPa, not annealed | 143 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 118 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability (1.00 mm) | 100 | mm/min | ISO 3795 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 30.0 - 50.0 | °C | |
| Holding Pressure | 30.0 - 60.0 | MPa |
| Injection instructions |
|---|
| Feeding Temperature: 40 - 80 °CMass Temperature: 220 - 260 °CBack Pressure: Low to MediumScrew Speed: Low to MediumFlow Front Speed: 100 - 200 mm/s |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PP Random Copolymer RP200 | M. Holland Company | PP Random Copolymer | MTEGRITY™ PP Random Copolymer |
| XENOY™ HX6600HP resin | SABIC Innovative Plastics Europe | PC+PBT | XENOY™ |
| Axiall PVC 38901 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Elastron® G G300.D50.B | Elastron USA, Inc. | SEBS | Elastron® G |
| POLIMAXX 3325M | IRPC Public Company Limited | PP Random Copolymer | POLIMAXX |