Adiprene® L 100
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6bhQLE_Adiprene-L-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ADIPRENE L 100 urethane elastomer is one of a series of liquid urethane polymers which can be cured to a strong, rubbery solid by reaction of the isocyanate groups with polyamine compounds. When cured with MBCA¹ curing agent, ADIPRENE L 100 yields vulcanizates in the 88 to 92 Shore A hardness range. Lower hardness values and special properties can be obtained with other curing systems. Cured ADIPRENE L 100 has high tensile strength and resilience, as well as excellent resistance to abrasion, compression set, oils, solvents, oxidation, ozone, and low temperatures. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 90 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 7.58 | MPa | |
| 300% Strain | 14.5 | MPa | |
| Tensile Strength | 31.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 450 | % | ASTM D412 |
| Tear Strength | |||
| -- 1 | 70.1 | kN/m | ASTM D624 |
| Split | 13 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 27 | % | ASTM D395B |
| Bayshore Resilience | 45 | % | ASTM D2632 |
| Clash-Berg Modulus | ASTM D1043 | ||
| -57°C | 210 | MPa | |
| -40°C | 73.1 | MPa | |
| -18°C | 22.4 | MPa | |
| 24°C | 17.9 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| CLTE - Flow | ASTM D696 | ||
| -36 to 0°C | 2.6E-4 | cm/cm/°C | |
| 0 to 24°C | 1.8E-4 | cm/cm/°C | |
| 24 to 100°C | 1.7E-4 | cm/cm/°C | |
| 100 to 150°C | 1.6E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.13 | W/m/K | ASTM C177 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 12 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Pot Life (100°C) | 10 | min | |
| Demold Time (100°C) | 30 to 45 | min | |
| Post Cure Time (70°C) | 16 | hr |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Abrasion Index - NBS | 175 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (100°C) | 1.0 | hr |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 6 GBF 3010 H | A. Schulman Europe | Nylon 6 | SCHULAMID® |
| SLOVAMID® 66/6 CF 30 | Plastcom | Nylon 66/6 | SLOVAMID® 66/6 |
| Norpex® PPE AX265 | Custom Resins Group | PPE | Norpex® |
| ColorRx® PCPT-1000NB | LTL Color Compounders, Inc. | PC+PET | ColorRx® |
| Grilon® BM-30 FR | EMS-GRIVORY | Nylon 6 | Grilon® |