Bergamid™ A70 G60 natural
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergamid™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6bN0bS_BergamidA70G60natural.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bergamid™A70 G60 natural is a polyamide 66 (nylon 66) product, which contains a 60% glass fiber reinforced material. It can be processed by injection molding and is available in Europe. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.70 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C, 4.00 mm) | 19000 | MPa | ISO 527-2/1 |
| Tensile Strength 1(23°C, 4.00 mm, Injection Molded) | 250 | MPa | ISO 527 |
| Tensile Strain (Break) | 2.4 | % | ISO 527 |
| Flexural Modulus | 18000 | MPa | ISO 178 |
| Flexural Strength | 342 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 250 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | °C | ISO 75-2/A |
| Continuous Use Temperature | 130 | °C | IEC 216 |
| Melting Temperature (DSC) | 255 - 265 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1481 N | RTP Company | PESU | RTP |
| Tufpet PBT B39 | Mitsubishi Rayon America Inc. | PBT | Tufpet |
| KumhoSunny PC/ABS HAC8265FR | Shanghai KumhoSunny Plastics Co., Ltd. | PC+ABS | KumhoSunny PC/ABS |
| Panlite® ML-5206ZLP | TEIJIN LIMITED | PC | Panlite® |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 8271 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |