Generic Nylon 66 - Carbon Fiber
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6bGAlV_Generic-Nylon-66---Carbon-Fiber.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Carbon Fiber This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.16 - 1.38 | g/cm³ | ASTM D792 |
| 23°C | 1.17 - 1.39 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.096 - 0.42 | % | ASTM D955 |
| Transverse flow : 23°C | 0.36 - 2.0 | % | ASTM D955 |
| 23°C | 0.18 - 0.74 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.40 - 1.0 | % | ASTM D570 |
| 23°C, 24 hr | 0.99 - 1.0 | % | ISO 62 |
| Saturated, 23°C | 4.5 - 5.6 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.75 - 2.2 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 118 - 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 7240 - 32800 | MPa | ASTM D638 |
| 23°C | 7810 - 26700 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 105 - 242 | MPa | ASTM D638 |
| Yield, 23°C | 130 - 243 | MPa | ISO 527-2 |
| Fracture, 23°C | 131 - 268 | MPa | ASTM D638 |
| Fracture, 23°C | 124 - 296 | MPa | ISO 527-2 |
| 23°C | 126 - 276 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 1.5 - 3.6 | % | ASTM D638 |
| Yield, 23°C | 1.3 - 7.6 | % | ISO 527-2 |
| Fracture, 23°C | 0.90 - 4.1 | % | ASTM D638 |
| Fracture, 23°C | 1.4 - 3.1 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5990 - 23400 | MPa | ASTM D790 |
| 23°C | 4630 - 24000 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 174 - 415 | MPa | ASTM D790 |
| 23°C | 180 - 440 | MPa | ISO 178 |
| Yield, 23°C | 159 - 368 | MPa | ASTM D790 |
| Fracture, 23°C | 237 - 410 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 129 - 172 | MPa | ASTM D695 |
| Coefficient of Friction | 0.081 - 0.36 | ASTM D1894 | |
| Wear Factor | 11 - 18 | 10^-8 mm³/N·m | ASTM D3702 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.0 - 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 24 - 67 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 27 - 110 | J/m | ASTM D256 |
| 23°C | 4.1 - 11 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 410 - 1100 | J/m | ASTM D256 |
| 23°C | 24 - 69 | kJ/m² | ISO 180 |
| Instrumented Dart Impact | |||
| 23°C | 5.20 - 15.5 | J | ASTM D3763 |
| 23°C | 1.70 - 3.99 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 253 - 263 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 249 - 261 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 231 - 262 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 239 - 251 | °C | ISO 75-2/A |
| Continuous Use Temperature | 119 - 120 | °C | ASTM D794 |
| Vicat Softening Temperature | 200 - 260 | °C | ISO 306 |
| Melting Temperature (DSC) | 260 - 265 | °C | ISO 3146 |
| Linear thermal expansion coefficient | |||
| Flow | 2.0E-6 - 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flow | 1.1E-5 - 8.3E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.1E-5 - 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 8.0E-6 - 1.0E-4 | cm/cm/°C | ASTM D696 |
| Lateral | 1.3E-5 - 4.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 1.0E-5 - 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | |||
| 23°C | 0.39 - 1.2 | W/m/K | ASTM C177 |
| 23°C | 0.28 - 1.0 | W/m/K | ISO 8302 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 2.5 - 1.2E+10 | ohms | ASTM D257 |
| -- | 10 - 2.5E+10 | ohms | IEC 60093 |
| Volume Resistivity | |||
| 23°C | 5.1 - 2.5E+10 | ohms·cm | ASTM D257 |
| 23°C | 5.0 - 2.5E+10 | ohms·cm | IEC 60093 |
| Insulation Resistance (23°C) | 1.0E+2 - 2.5E+10 | ohms | IEC 60167 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.8 - 106 | °C | |
| Drying Time | 2.9 - 11 | hr | |
| Suggested Max Moisture | 0.097 - 0.20 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 280 - 301 | °C | |
| Nozzle Temperature | 288 - 291 | °C | |
| Processing (Melt) Temp | 286 - 294 | °C | |
| Mold Temperature | 79.0 - 106 | °C | |
| Injection Pressure | 96.1 - 104 | MPa | |
| Back Pressure | 0.172 - 0.517 | MPa | |
| Screw Speed | 45 - 46 | rpm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic Nylon 66 - Carbon FiberThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo PP FY2011E | Sumitomo Chemical Asia | PP Homopolymer | Sumitomo PP |
| TIPPLEN® R 1059 A | MOL Petrochemicals Co. Ltd. | PP Random Copolymer | TIPPLEN® |
| Niuk 70GP20 | Shanghai Niuk New Plastic Technology Co., Ltd. | AS | Niuk |
| FHR Polypropylene 23R2A | Flint Hills Resources, LP | PP Random Copolymer | FHR Polypropylene |
| Dryflex® WS 25E950 | ELASTO | TPE | Dryflex® |