Order Products : sales@su-jiao.com
Amodel® AT-6130 HS
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Amodel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6aH73g_Amodel-AT-6130-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amodel AT -6130 HS is a 30% glass fiber reinforced and toughened poly (phthalamide) (PPA) resin with higher elongation than other 30% glass fiber reinforced Amodel resin. Specially developed for car snap-on electronic connectors. Good fluidity and short molding cycle. The process window is relatively wide, and the mold temperature can be as low as 150 °F (65°C). -black: AT-6130 HS BK 324 -natural color: AT-6130 HS NT |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.34 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.50 | -- | % | ASTM D955 |
| Transverse flow | 0.80 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | -- | % | ASTM D570 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9310 | -- | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Fracture | 167 | -- | MPa | ASTM D638 |
| Fracture | 170 | -- | MPa | ISO 527-2 |
| Tensile Elongation | ||||
| Fracture | 3.2 | -- | % | ASTM D638 |
| Fracture | 3.3 | -- | % | ISO 527-2 |
| Flexural Modulus | ||||
| -- | 7860 | -- | MPa | ASTM D790 |
| -- | 7580 | -- | MPa | ISO 178 |
| Flexural Stress | ||||
| -- | 225 | -- | MPa | ISO 178 |
| Yield | 236 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 13 | -- | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | 130 | -- | J/m | ASTM D256 |
| Unnotched Izod Impact | 1400 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 298 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 276 | -- | °C | ISO 75-2/A |
| Melting Temperature | ||||
| -- | 310 | -- | °C | ISO 11357-3 |
| -- | 306 | -- | °C | ASTM D3418 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 316 - 324 | °C | |
| Front Temperature | 327 - 332 | °C | |
| Processing (Melt) Temp | 321 - 335 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Rate | Fast |
| Injection instructions |
|---|
| 射出压力：2~4英寸/秒（5-10厘米/秒）之间。保压压力调整为射出压力的1/2。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TA210GR | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| ExxonMobil™ LLDPE LL 3001.32 Cast | ExxonMobil Chemical | LLDPE | ExxonMobil™ LLDPE |
| EGYPTENE HD 5226 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |
| LIM™ 6071 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | LIM™ |
| Petrothene® GA605 | LyondellBasell Industries | LLDPE | Petrothene® |