Polylink Polymer P-11060-CT

Category:	TPO , Compounded Polypropylene
Manufacturer:	Polylink Polymers (India) Ltd.
Trademark:	Polylink Polymer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	6ZVx92_Polylink-Polymer-P-11060-CT.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

P-11060-CT in manufactured by compounding polypropylene Homo-polymer with fine grade of chalk & talc, suitable processing aids, heat stabilizers and anti oxidants. This injection molding grade is specially designed for grade furniture and house hold application. Filed ppcounds for garden furniture

The filler in the compound incorporates certain important those are essential for ultimate product.
The properties are as under.

Improves mechanical property.

Improves gloss, Service temperature.

Improves dimension stability etc.

Reduces cost.

Reduce cycle time.

Reduces shrinkage etc.

General Information
Filler / Reinforcement	Chalk filler, 60% filler by weight Talc filler, 60% filler by weight
Features	Homopolymer
Uses	Furniture
Appearance	White
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	< 1.45	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	4.5 - 6.5	g/10 min	ASTM D1238
Moisture Content	< 600	ppm	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	17.2	MPa	ASTM D638
Tensile Elongation (Break)	10	%	ASTM D638
Flexural Modulus	3430	MPa	ASTM D790
Flexural Strength	26.5	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	25	J/m	ASTM D256

Extrusion	Nominal Value	Unit
Drying Temperature	70.0	°C
Cylinder Zone 1 Temp.	160 - 170	°C
Cylinder Zone 2 Temp.	180 - 190	°C
Cylinder Zone 3 Temp.	200	°C
Cylinder Zone 4 Temp.	210	°C
Cylinder Zone 5 Temp.	220	°C

Extrusion instructions
Zone 6 : 230°C - 235°C

Resin Grade	Manufacturer	Category	Trademark
MARPOL® LL4F 808-SB	Marco Polo International, Inc.	LLDPE	MARPOL®
Nipol® LX820A	Zeon Corporation	Latex	Nipol®
Fibremod™ GE225U	Borealis AG	TPO	Fibremod™
ECOVYLOPET® EMC2311	TOYOBO America, Inc.	PET	ECOVYLOPET®
Sylvin 9764-60D Natural	Sylvin Technologies Incorporated	PVC, Rigid	Sylvin