Novodur® E309
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Styrolution |
| Trademark: | Novodur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ZKOuG_Novodur-E309.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Novodur E309 is a extrusion grade especially designed for furniture profiles |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.50 to 0.70 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 95.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2200 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 43.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 2.7 | % | ISO 527-2 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 100 | kJ/m² | |
| 23°C | 140 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C | 11 | kJ/m² | |
| 23°C | 21 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 95.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 95.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 100 | °C | ISO 306/B50 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.10 | ||
| 1 MHz | 2.90 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 5.0E-3 | ||
| 1 MHz | 9.0E-3 | ||
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 260 | °C | |
| Mold Temperature | 70.0 | °C | |
| Injection Velocity | 240 | mm/sec |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Melt Temperature | 220 to 260 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P3935T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| VESTAMID® E E58-S4 | Evonik Industries AG | Nylon 12 | VESTAMID® E |
| Huafon JF-PDY-P531H | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| INEOS PP 401-CA55 | INEOS Olefins & Polymers Europe | PP Impact Copolymer | INEOS PP |
| Karina BEIGE COLOR CONCENTRATE 08/240-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |