ZYLAR® 670
| Category: | MMBS , Methyl Methacrylate Butadiene Styrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | ZYLAR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6ZFPVp_ZYLAR-670.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Zylar 670 is an impact modified styrene acrylic copolymer that provides practical toughness, excellent clarity and superior processing characteristics for demanding injection molded applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.05 | g/cm³ | ASTM D792 |
| -- | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 6.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.60 | % | ASTM D955 |
| -- | 0.20 to 0.60 | % | ISO 294-4 |
| Water Absorption | |||
| Saturation, 23°C | 0.10 | % | ASTM D570, ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 70 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- | 1830 | MPa | ASTM D638 |
| -- | 1800 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 27.6 | MPa | ASTM D638 |
| Yield, 23°C | 28.0 | MPa | ISO 527-2 |
| Tensile Elongation (Break) | 42 | % | ASTM D638 |
| Flexural Modulus | |||
| -- | 1830 | MPa | ASTM D790 |
| -- | 1800 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 41.4 | MPa | ASTM D790 |
| -- | 41.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Gardner Impact | 7.91 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 97.8 | °C | ASTM D1525 1 |
| Maximum Service Temperature | 250 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 2 | 1.560 | ASTM D542, ISO 489 | |
| Transmittance (550 nm) | 91.0 | % | ASTM D1003 |
| Haze | 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 185 to 220 | °C | |
| Front Temperature | 190 to 225 | °C | |
| Processing (Melt) Temp | 200 to 240 | °C | |
| Mold Temperature | 30.0 to 55.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h), Loading 1 (10 N) |
| 2 . | Sodium D Line |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS 391MM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| GAPEX® RPP20EU78BK | Ferro Corporation | PP, Unspecified | GAPEX® |
| Geon™ Vinyl Rigid Molding 87402 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| Epic Urethane S7381 | Epic Resins | PUR, Unspecified | Epic Urethane |
| KYOCERA KE-200DC-1 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |