SABIC® STAMAX 20YK270 resin
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® STAMAX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6Z8xZD_SABIC-STAMAX-20YK270-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SABIC® STAMAX 20YK270 is a 20% long glass fiber reinforced polypropylene with improved impact and flow properties. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 80929423. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792, ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| -- | 4450 | MPa | ISO 527-2/1 |
| 80°C | 3250 | MPa | ISO 527-2/1 |
| 120°C | 2850 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Fracture | 80.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 80°C | 54.0 | MPa | ISO 527-2/1A/50 |
| Fracture, 120°C | 40.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 2.4 | % | ISO 527-2/50 |
| Flexural Modulus 1 | ISO 178 | ||
| 64.0mm span | 3900 | MPa | ISO 178 |
| 80°C, 64.0mm span | 2850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 2 | 18 | kJ/m² | ISO 179/1eA |
| 23°C 3 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4 | ISO 179/1eU | ||
| -30°C | 56 | kJ/m² | ISO 179/1eU |
| 23°C | 49 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact 5(23°C) | 17 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy 6(23°C, Energy to Peak Force) | 4.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7(1.8 MPa, Unannealed) | 156 | °C | ISO 75-2/A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Fiber Content | 20 | % | ISO 3451 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 - 290 | °C | |
| Middle Temperature | 225 - 285 | °C | |
| Front Temperature | 220 - 280 | °C | |
| Nozzle Temperature | 220 - 280 | °C | |
| Processing (Melt) Temp | 220 - 280 | °C | |
| Mold Temperature | 20.0 - 80.0 | °C | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Screw Speed: Lowest Possible |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4mm, Cut |
| 3 . | 80*10*4 mm, Cut |
| 4 . | 80*10*4mm, Cut |
| 5 . | 80*10*4mm, Cut |
| 6 . | 6.6 m/sec |
| 7 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 2830 | Huntsman Corporation | PAO | REXtac® APAO |
| SCLAIR® 2712CC | NOVA Chemicals | HDPE | SCLAIR® |
| Shuang-Bang C-8207N | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| Telcar® GS7567 | Teknor Apex Asia Pacific PTE. LTD. | TPE | Telcar® |
| Amodel® AT-1001L | Solvay Specialty Polymers | PPA | Amodel® |