Order Products : sales@su-jiao.com
SCHULAMID® 66 MV HI H2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6Yzwks_SCHULAMID66MVHIH2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High impact modified Polyamide 66, Organic stsbilization |
| General Information | |
|---|---|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 26.0 | -- | cm³/10min | ISO 1133 |
| Viscosity Number (96% H2SO4) | 156 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2280 | 860 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | |||
| Yield | 58.0 | 40.0 | MPa | ISO 527-2/1A/50 |
| Fracture | 51.0 | 46.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 6.0 | 25 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 22 | 240 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 65 kJ/m² | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | -- | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 138 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 49.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 250 | -- | °C | ISO 306/A50 |
| -- | 210 | -- | °C | ISO 306/B50 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 60 - 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPH 3620WZ | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| Nanjing Hongrui PP P830 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PP, Unspecified | Nanjing Hongrui PP |
| FILLMA 5002F30A | POLYROCKS CHEMICAL CO., LTD | PP, Unspecified | FILLMA |
| Karina BLACK PVC COMPOUND 601-48/ 1-BY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® Satinice df23 8N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |