Nypol® PA A3 HF PRT0327 NR440 MSP
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6XODKI_Nypol-PA-A3-HF-PRT0327-NR440-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in black color, lubrificated. Ideal for injection molding, good set of thermal properties, electrical and mechanical. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.5 to 2.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 85.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 2750 | MPa | ASTM D790 |
| Flexural Strength | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 65.0 | °C | ASTM D648 |
| Peak Melting Temperature | 250 to 265 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 | |
| Glow Wire Ignition Temperature | 850 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 207A TFE 13 SI 2 HS | RTP Company | Nylon 6 | RTP |
| Unipren® Elastomers B3 PRTA010 55A UP314 | Petropol Industry and Trade of Polymers LTDA | TPV | Unipren® Elastomers |
| Arnitel® PM471 | DSM Engineering Plastics | TPC-ET | Arnitel® |
| LOXIM 220 01 HB | LOXIM Industries Private Limited | PBT | LOXIM |
| POTICON OA20 | Otsuka Chemical Co., Ltd. | Acetal (POM) Copolymer | POTICON |