Halene H Y5401
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene H |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6XNwcW_Halene-H-Y5401.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Y5401 is a HDPE monofilament grade produced by the Mitsui CX Technology. This grade is characterized by excellent processability and high mechanical strength. Y5401 can be used for stretch tapes, raffia and yarns for woven sacks & tarpaulin. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.954 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, Compression Molded) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield, molding | 25.0 | MPa | ASTM D638 |
| Fracture, molding | 35.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, Compression Molded) | > 500 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Compression Molded) | 250 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 122 | °C | ASTM D1525 3 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 200 - 240 | °C | |
| Cylinder Zone 2 Temp. | 200 - 240 | °C | |
| Cylinder Zone 3 Temp. | 200 - 240 | °C | |
| Cylinder Zone 4 Temp. | 200 - 240 | °C | |
| Cylinder Zone 5 Temp. | 200 - 240 | °C | |
| Die Temperature | 250 - 260 | °C |
| Extrusion instructions |
|---|
| Quench Temperature: 30°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Cellophane™ 335WS | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Estane® 2103-90AEFH TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| LNP™ STAT-KON™ SX90398 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ STAT-KON™ |
| Lupox® HV1010 | LG Chem Ltd. | PBT | Lupox® |
| Sylvin 83015-80FUV Grey 9615 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |