Tarnamid® T-30
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6WwVAg_Tarnamid-T-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tarnamid T-30 there is high viscosity polyamide 6. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 25.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 1.4 | -- | % | |
| Flow : 2.00 mm | 1.4 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % | |
| Viscosity Number | 240 | -- | cm³/g | ISO 307 |
| Relative Viscosity - H2SO4 (25°C) | 3.90 | -- |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Limit of Temperature - a few hours operation | < 180 | -- | °C | |
| Temperature Index | ||||
| 20000 hr | 70 | -- | °C | |
| 5000 hr | 85 | -- | °C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | + | -- | FMVSS 302 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA6, EN, 22-030 | -- | ISO 1874 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 140 | 60.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2800 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 78.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 100 | > 280 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2400 | 900 | MPa | ISO 178 |
| Flexural Stress 2 | 82.0 | 28.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -- | 6.0 | 13 | kJ/m² | |
| -30°C | 3.0 | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | No Break | No Break | ||
| -30°C | No Break | No Break | ||
| Notched Izod Impact Strength | 4.0 | 10 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | 50.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 195 | 180 | °C | ISO 306/B |
| Melting Temperature | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.1E-4 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 1.2E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+16 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength (2.00 mm) | 21 | 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 Hz) | 3.50 | 4.20 | IEC 60250 | |
| Dissipation Factor (1 Hz) | 0.022 | 0.20 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (3.20 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 50 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOYOBO Urethane A1061D | TOYOBO America, Inc. | PUR-Butyl | TOYOBO Urethane |
| Hanwha Total PP BI961 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| LEXAN™ EXL1463T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 9067F3 Red 6261 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LNP™ THERMOCOMP™ LF006 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |