TRIBOCOMP® PPA GF30 TS0
| Category: | PPA , Polyphthalamide |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6WENBl_TRIBOCOMP-PPA-GF30-TS0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIBOCOMP® PPA GF30 TS0 is a Polyphthalamide (PPA) product filled with 30% glass fiber. It is available in Europe. Primary characteristic: lubricated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.55 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.35 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.4 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 11300 | 11000 | MPa | |
| 90°C | 10300 | 7700 | MPa | |
| 120°C | 8800 | 4300 | MPa | |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 185 | 170 | MPa | |
| Yield, 90°C | 140 | 105 | MPa | |
| Yield, 120°C | 115 | 75.0 | MPa | |
| Tensile Strain (Break, 23°C) | 2.2 | 2.2 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10500 | 10000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 265 | 255 | MPa | ISO 178 |
| Coefficient of Friction 1 | ASTM D3702 | |||
| vs. Itself - Dynamic | 0.22 | -- | ||
| vs. Itself - Static | 0.18 | -- | ||
| Wear Factor (23°C) | 23.0 | -- | ASTM D3702 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 50 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 300 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 285 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.5E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.30 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Electric Strength | 35 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.080 | % | |
| Rear Temperature | 320 to 340 | °C | |
| Middle Temperature | 320 to 335 | °C | |
| Front Temperature | 320 to 335 | °C | |
| Nozzle Temperature | 325 to 340 | °C | |
| Processing (Melt) Temp | < 340 | °C | |
| Mold Temperature | 135 to 165 | °C |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Badamid® LA70 H | Bada AG | Nylon 66 | Badamid® |
| Dryflex® WS 40E450 | ELASTO | TPE | Dryflex® |
| Hanwha Total PP TB24 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, HMS | Hanwha Total PP |
| Karina PVC COMPOUND E-85/227-D-AT-IS-SI | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POCAN® KL 1-7033 000000 | LANXESS GmbH | PBT | POCAN® |