INEOS PP L40N-00
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | INEOS Olefins & Polymers USA |
| Trademark: | INEOS PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6W5EAt_INEOS-PP-L40N-00.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| L40N-00 is a high melt flow rate, nucleated polypropylene impact copolymer designed for injection molding applications. L40N-00 is suitable for injection molding a wide variety of products where fast molding cycles and part durability are both desired. This material meets the requirements of the U.S. Food and Drug Administration as specified in 21 CFR 177.1520. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 79 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 22.5 | MPa | |
| Break | 16.6 | MPa | |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.9 | % | |
| Break | 58 | % | |
| Flexural Modulus - 1% Secant | 1100 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 59 | J/m | |
| 23°C | 120 | J/m | |
| Notched Izod Impact (Area) | ASTM D256 | ||
| -20°C | 5.70 | kJ/m² | |
| 23°C | 12.1 | kJ/m² | |
| Instrumented Impact, Ductility | ASTM D3763 | ||
| -20°C | Mixed | ||
| 23°C | Ductile |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 98.9 | °C | |
| 1.8 MPa, Unannealed | 53.9 | °C | |
| Vicat Softening Temperature | 145 | °C | ASTM D1525 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (60°) | 64 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niche PPCT40BK | Niche Polymer, LLC | PP Copolymer | Niche |
| Andur AL 70 DP/Curene® 110 | Anderson Development Company | PUR-Eth,aliphat | Andur |
| Generic Acetal (POM) Copolymer - Glass Fiber | Generic | Acetal (POM) Copolymer | Generic |
| Hytrel® G4774 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| MARPOL® mLLF 801-B | Marco Polo International, Inc. | mLLDPE | MARPOL® |