TOTAL Polystyrene 1450
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | TOTAL Refining & Chemicals |
| Trademark: | TOTAL Polystyrene |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6VvrN9_TOTAL-Polystyrene-1450.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polystyrene Crystal 1450 is a high heat resistant, easy flow polystyrene for foam extrusion and injection molding applications. It offers optimum fluidity and excellent thermal properties for foam extrusion and injection molding. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Apparent Density | 0.60 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 5.0 | g/10 min | ASTM D1238, ISO 1133 |
| Spiral Flow 1 | 55.0 | cm | ASTM D3123 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption | |||
| Saturation | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| L scale, 23°C, injection molding | 70 | ASTM D785 | |
| L scale, 23°C | 70 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C, Injection Molded) | 50.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, 23°C, Injection Molded) | 2.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus (23°C, Injection Molded) | 3300 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact | |||
| 23°C, injection molding | 73 | J/m | ASTM D256 |
| 23°C, injection molding | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 103 | °C | ISO 306/A50, ASTM D1525 2 |
| CLTE - Flow | 8.9E-5 | cm/cm/°C | ASTM D696 |
| Heat Distortion | |||
| -- | 85 | °C | ISO 75-2 |
| -- | 85 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | IEC 60093 |
| Dielectric Strength | 150 | kV/mm | ASTM D149 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 220 | °C | |
| Front Temperature | 210 - 240 | °C | |
| Nozzle Temperature | 210 - 240 | °C |
| Injection instructions |
|---|
| Zone 4: 210-240°C |
| Note Message | |
|---|---|
| 1 . | Melt temperature: 220°C |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANAMID 6 B12^FC | Polykemi AB | Nylon 6 | SCANAMID 6 |
| Starex VE-0858 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Innova Clear R 350L G2 | Innova SA | PS (HIPS) | Innova |
| SCHULAMID® 612 GF 33 H2 | A. Schulman Europe | Nylon 612 | SCHULAMID® |
| PERLAS® O07F2000B00 | A.D. Compound S.p.A. | PP Homopolymer | PERLAS® |