HANWHA LDPE 5305
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6TO6Vs_HANWHA-LDPE-5305.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LDPE 5305 is manufactured by DOW tubular high pressure process and designed for variety of film application such as high transparent package film. LDPE 5305 has well balanced property of high clarity, mechanical property and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.921 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 10.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 21.6 | MPa | ASTM D882 |
| TD : Break, 30 µm | 18.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 350 | % | ASTM D882 |
| TD : Break, 30 µm | 550 | % | ASTM D882 |
| Dart Drop Impact (30 µm) | 85 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 30.0 µm | 88.3 | kN/m | ASTM D1004 |
| TD : 30.0 µm | 83.4 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 88.0 | °C | ASTM D1525 |
| Melting Temperature | 110 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 6.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 140 - 170 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.025 to 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYTROPE® STR 3568EU-01 NATURAL | A. Schulman Inc. | Polyolefin, Enhanced (Capstock Resin) | POLYTROPE® |
| Sup-tech P280 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Ultramid® C33 01 | BASF Corporation | Nylon 66/6 | Ultramid® |
| Durethan® B 40 F 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| HiFill® PA6 IM L | Techmer Engineered Solutions | Nylon 6 | HiFill® |