DOWLEX™ NG 2049B
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 6TIokk_DOWLEX-NG-2049B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ NG 2049B is a Linear Low Density Polyethylene, 1-Octene copolymer, produced with the SOLUTIONTM technology. This resin is an excellent option when an increase in modulus is required while maintaining mechanical properties. This resin presents outstanding optical properties, allowing high quality impression. Main Characteristics:
Complies with:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.926 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 38 | µm | |
| Film Puncture Resistance (3700 µm) | 10.0 | J/cm³ | Internal method |
| secant modulus | ASTM D882 | ||
| 2% secant, MD | 235 | MPa | ASTM D882 |
| 2% secant, TD | 281 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 38 µm | 13.0 | MPa | ASTM D882 |
| TD : Yield, 38 µm | 15.0 | MPa | ASTM D882 |
| MD : Fracture, 38 µm | 48.0 | MPa | ASTM D882 |
| TD : Fracture, 38 µm | 42.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 38 µm | 630 | % | ASTM D882 |
| TD : Fracture, 38 µm | 740 | % | ASTM D882 |
| Dart Drop Impact (38 µm) | 220 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 350 | g | ASTM D1922 |
| TD : 38 µm | 800 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 37.5 µm) | 80 | ASTM D2457 | |
| Haze (37.5 µm) | 9.0 | % | ASTM D1003 |
| Additional Information |
|---|
| 吹塑薄膜的加工条件： 模具间隙：0.8-2-8 mm 熔体温度：190 - 250 °C 放大比：1.5 - 3.5 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ PS High Impact IS210 | M. Holland Company | PS (HIPS) | MTEGRITY™ PS High Impact |
| BESTNYL SI30VI02BX | Triesa Plastics | Nylon 6 | BESTNYL |
| Axiall PVC 22902 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Grivory® HTV-4H1 nat | EMS-GRIVORY | Nylon 6I/6T | Grivory® |
| Dryflex® VE 70A101 | ELASTO | TPV | Dryflex® |